Effect of butylated hydroxytoluene (BHT) concentrations on polymerization shrinkage stress and other physicochemical properties of experimental resin composites.

The present study examined different concentrations of the butylated hydroxytoluene (BHT) inhibitor on the kinetics of conversion, polymerization shrinkage stress, and other correlated physicochemical properties of experimental resin composites (ERC). A model composite was formulated with 75 wt% filler containing 0.5 wt% camphorquinone and 1 wt% amine with BHT concentrations of 0.01 wt% (BHT-0.01); 0.1 wt% (BHT-0.1); 0.25 wt% (BHT-0.25); 0.5 wt% (BHT-0.5); 1 wt% (BHT-1), and control (no BHT). They were tested on polymerization shrinkage stress (PSS; n = 5), degree of conversion (DC; n = 3), maximum polymerization rate (Rp; n = 5), water sorption (W; n = 0), and solubility (W; n = 10), flexural strength (FS; n = 10), flexural modulus (FM; n = 10), Knoop microhardness (KH; n = 10), and microhardness reduction (HR; n = 10). Data concerning these tests were submitted to one-way ANOVA and Tukey's test (α = 0.05; β = 0.2). BHT-0.25, BHT-0.5, and BHT-1 showed a gradually significant decrease in PSS (p = 0.037); however, BHT-1 demonstrated a decrease in the physicochemical properties tested. Thus, within the limitations of this study, it was possible to conclude that BHT concentrations between 0.25 and 0.5 wt% are optimal for reducing shrinkage stress without affecting other physicochemical properties of ERCs.

Copyright © 2024 Elsevier Ltd. All rights reserved.