Experimental magnesium phosphate cement paste increases torque of trochanteric fixation nail advanced™ blades in human femoral heads.

BACKGROUND

The use of polymethylmethacrylate cement for in-situ implant augmentation has considerable disadvantages: it is potentially cytotoxic, exothermic and non-degradable. Therefore, the primary aim of this study was to develop a magnesium phosphate cement which meets the requirements for in-situ implant augmentation as an alternative. Secondly, this experimental cement was compared to commercial bone cements in a biomechanical test set-up using augmented femoral head blades.

METHODS

A total of 40 human femoral heads were obtained from patients who underwent total hip arthroplasty. After bone mineral density was quantified, specimens were assigned to four treatment groups. A blade of the Trochanteric Fixation Nail Advanced™ was inserted into each specimen and augmented with either Traumacem™ V+, Paste-CPC, the experimental magnesium phosphate cement or no cement. A rotational load-to-failure-test (0° to 90°) was performed.

FINDINGS

A conventional two-component magnesium phosphate cement failed in-situ implant augmentation consistently due to filter pressing. Only a glycerol-based magnesium phosphate paste was suitable for the augmentation of femoral head blades. While the blades augmented with Traumacem™ V+ yielded the highest maximum torque overall (22.1 Nm), the blades augmented with Paste-CPC and the magnesium phosphate paste also showed higher maximum torque values (15.8 and 12.8 Nm) than the control group (10.8 Nm).

INTERPRETATION

This study shows for the first time the development of a degradable magnesium phosphate cement paste which fulfills the requirements for in-situ implant augmentation. Simultaneously, a 48% increase in stability is demonstrated for a scenario where implant anchorage is difficult in osteoporotic bone.