Experimental resin-based dual-cured calcium aluminate and calcium titanate materials for vital pulp therapy.

This paper evaluates the physicochemical and biological properties of experimental resin-based dual-cured calcium aluminate (CA) and calcium titanate (CTi) materials for vital pulp therapy (VPT). The experimental dual-cured materials were obtained as two pastes: a) Bis-EMA 10, PEG 400, DHEPT, EDAB, camphorquinone, and butylated hydroxytoluene; and b) fluoride ytterbium, Bis-EMA 10, Bis-EMA 30, benzoyl peroxide, and butylated hydroxytoluene. The materials were divided into six groups based on the added calcium component: MTA (MTA®, Angelus); CLQ (Clinker-Fillapex®, Angelus); CA (calcined at ,1200°C in pastes a and b); CA800 (calcined at 800°C in paste a); CA1200 (calcined at 1,200°C in paste a); and CTi (paste a). The real-time degree of conversion and rate of polymerization (n = 3), diametral tensile strength (n = 10), hydrogen potential (n = 15), calcium ion release (n = 10), water sorption and solubility (n = 10), and cell viability (n = 6) were evaluated. One- and two-way ANOVA and Tukey's post hoc test were used in the analysis of the parametric data, and Kruskal-Wallis and Dunn's multiple tests were used to analyze the nonparametric data (α = 0.05). CLQ, CA800 and CA1200 had the highest diametral tensile strength. The water solubility of MTA was similar to that of CA800, CA1200 and CTi. CA800 and CA1200 resulted in cell viabilities similar to those of MTA and CLQ. The experimental dual-cured CA-based material that calcined at 800°C showed physicochemical and biological properties suitable for VPT, and similar to those of MTA.