Can we expect similar behavior among CuNiTi 35°C wires?

OBJECTIVE

This paper aims to verify the thermodynamic, mechanical and chemical properties of CuNiTi 35ºC commercial wires.

METHODS

Forty pre-contoured copper-nickel-titanium thermodynamic 0.017 x 0.025-in archwires with an Af temperature of 35°C were used. Eight wires from five different manufacturers (American Orthodontics® [G1], Eurodonto® [G2], Morelli® [G3], Ormco® [G4] and Orthometric® [G5]) underwent cross-sectional dimension measurements, tensile tests, SEM-EDS and differential scanning calorimetry (DSC) tests. Parametric tests (One-way ANOVA and Tukey post-test) were used, with a significance level of 5%, and Pearson's correlation coefficient test was performed between the Af and chemical elements of the wires. All sample tests and statistical analyses were double-blinded.

RESULTS

All wires presented standard dimensions (0.017 x 0.025-in) and superelastic behavior, with mean plateau forces of: G1 = 36.49N; G2 = 27.34N; G3 = 19.24 N; G4 = 37.54 N; and G5 = 17.87N. The Af means were: G1 = 29.40°C, G2 = 29.13°C and G3 = 31.43°C, with p>0.05 relative to each other. G4 (32.77°C) and G5 (35.17°C) presented statistically significant differences between each other and among the other groups. All samples presented Ni, Ti, Cu and Al in different concentrations.

CONCLUSIONS

The chemical concentration of the elements that compose the alloy significantly influenced the thermodynamic and mechanical properties.