Grindability of cast Ti-6Al-4V alloyed with copper.

PURPOSE

This study investigated the grindability of cast Ti-6Al-4V alloyed with copper.

MATERIALS AND METHODS

The metals tested were commercially pure titanium (CP Ti), Ti-6Al-4V, experimental Ti-6Al-4V-Cu (1, 4, and 10 wt% Cu), and Co-Cr alloy. Each metal was cast into five blocks (3.0 x 8.0 x 30.0 mm(3)). The 3.0-mm wide surface of each block was ground using a hand-piece engine with an SiC wheel at four circumferential speeds (500, 750, 1000, and 1250 m/min) at a grinding force of 100 g. The grindability index (G-index) was determined as volume loss (mm(3)) calculated from the weight loss after 1 minute of grinding and the density of each metal. The ratio of the metal volume loss and the wheel volume loss was also calculated (G-ratio, %). Data (n = 5) were statistically analyzed using ANOVA (alpha= 0.05).

RESULTS

Ti-6Al-4V and the experimental Ti-6Al-4V-Cu alloys exhibited significantly (p < 0.05) higher G-indexes compared with CP Ti and Co-Cr at any rotational speed except for the lowest speed (500 m/min). At 500 m/min, the G-index of Ti-6Al-4V-Cu increased as the amount of alloyed copper increased. The 4% Cu and 10% Cu alloys had significantly greater G-indexes than did 1% Cu and Ti-6Al-4V at the highest rotational speed (1250 m/min). Increasing the percentage of alloyed copper and the circumferential speed also increased the G-ratio.

CONCLUSIONS

A slight reduction in ductility due to alloying Ti-6Al-4V with copper improved the grindability of some of the resultant Ti-6Al-4V-Cu alloys.